Can you reuse oil for quenching?

Usually, the post-quench washer is used to recover the quench oil for reuse. This washer must only be used to clean parts after the quench and must not be contaminated with other coolants or other contaminants. In this process, the oil is recovered from the post-quench wash and segregated to a separate tank.

Can you use used oil for quenching?

While not specifically designed for it, both new and used engine oils can be used for quenching. They're popular because of their low cost, and they provide adequate performance. Used motor oil is fairly cheap or even free, but it can contain contaminants from previous use.

How long is quenching oil good for?

Quenching and martempering oils deteriorate during use, although most premium quenching oils can last more than 10 years when given reasonable use and care.

Is it better to quench steel in oil or water?

Water-quenched steels will generally be harder than oil-quenched steels. This is mainly because the thermal conductivity of water is higher than the thermal conductivity of most oils (that I know); consequently, the rates of cooling will be less rapid (or lower) in oils compared with water.

Why is oil used instead of water in quenching?

Oil has a slower rate of cooling compared to either water or brine, but faster than air, making it an intermediate quench.

Forged in Fire: Forging Tips: How to Use the Quench (Season 3) | History

What liquid do blacksmiths use to quench?

Blacksmiths generally use water, oil, or compressed air to quench. These substances vary in environmental impact, cost, and effects on the metal, but the best quenching medium is usually water or quenching oil.

Why do you preheat quench oil?

I figure preheating the oil does one of two things. It either lowers the shock for the quench, making fractures and bends less likely (hope it's this one, because it didn't happen) or it hardens better because it makes the oil less viscous, meaning it can transfer heat away from the blade better.

Can you use vegetable oil to quench steel?

There are many food-grade quenching oil options available to use for blacksmithing. Among these options are vegetable, peanut, and avocado oil. Some commonly used vegetable oils are canola, olive, and palm kernel oil.

What are the disadvantages of quenching steel?

There are several impacts that should be noted about quenching a material. First, the impact on microstructure can wholly depend on the quenching process and how long it was held at certain temperatures. The percentage carbon in the steel can also impact on the time needed to obtain different forms of the steel.

Can you oil harden mild steel?

Pure steel is actually too soft for many applications. In order to put a hard layer on the steel, carbon must be fused at the molecular level into the top centimeter or so of the steel. One way to do this is to make the steel red-hot, then plunge it into motor oil.

Can you use vegetable oil to quench knives?

No. IF one were to quench 1095 in vegetable oil. make sure that it is canola, and that its at least 120F (140F is better) hot before you quench into it. also make sure to grind the steel thin before heat treating.

How hot does oil have to be to quench?

Quenching into oil above 212°F (100°C) has traditionally been referred to as "hot oil" quenching. Oil temperatures in the 195°F - 450°F (90°C - 230°C) range have been used with both ends of the spectrum normally reserved for special applications.

How long should you quench a blade?

For the blade to harden, it needs to cool below 900℉. Wait about 10 to 15 seconds before pulling the blade out and checking it for warping.

What motor oil is best for quenching?

Canola, Motor Oil, and the Inconel Probe Test

I found a study on 1045 steel where they found canola to quench more rapidly than motor oil so I am going to stick with canola as my “cheap” quenching option to test.

What quench oil is used on forged in fire?

As those of you who make knives know, there are several different quench oils out there, but they really fall into 2 main speeds/categories. These are fast and medium speed oils, and the most widely used products on the market are Parks 50 (fast) and AAA (medium). The best oil to use depends on the steel in question.

Why do blacksmiths quench in oil?

Hot oils are kept at much higher temperatures and are used to ensure that a part's core temperature and surface temperature do not vary too greatly during a quench. This controls distortion and reduces the risk of cracking.

How hot does steel have to be to quench?

The process of quenching is a progression, beginning with heating the sample. Most materials are heated to between 815 and 900 °C (1,500 to 1,650 °F), with careful attention paid to keeping temperatures throughout the workpiece uniform.

How do you make steel harder but not brittle?

To make steel harder, it must be heated to very high temperatures. The final result of exactly how hard the steel becomes depends on the amount of carbon present in the metal. Only steel that is high in carbon can be hardened and tempered.

Can you over temper steel?

While you can definitely over-temper a blade, that will leave it too soft rather than too brittle; you can also over-harden (or, rather, under-temper) it, which will leave it very hard and very brittle.

Which is used as common quenching agent?

Despite reports of decomposition of DBPs caused by some quenching agents, particularly sulphite and thiosulphate, a survey of the literature shows that they are still the most commonly used quenching agents in analysis of DBPs.

Is Parks 50 a fast quench oil?

Parks 50 is considered a fast oil. Many times a quench oil is described in seconds quenching using a Nickel Ball test. The Nickel Ball quench time is 7-9 seconds.

Does quenching make metal brittle?

Quenching results in a metal that is very hard but also brittle. Gently heating a hardened metal and allowing it to cool slowly will produce a metal that is still hard but also less brittle.

Does quenching increase strength?

Quench Hardening Steel

Depending on the carbon content and alloying elements of the steel, it can get left with a harder, more brittle microstructure, such as martensite or bainite, when it undergoes the quench hardening process. These microstructures result in increased strength and hardness for the steel.

Can you quench a blade in mercury?

In order to quench your sword in mercury, you need to displace more than one and a half times its own weight in mercury - and you need to put a corresponding amount of pressure on the blade. However, quenching is done while the metal is still hot and partially malleable.